Richard Wrote : "If you pre heat the SS that is going to be welded and the
"I" beam and let it cool slow you will HAVE issues. "
HAVE is my emphasis added.
Richard: Hi, is this correct or did you mean to say you would NOT have
issues (annealing like on copper or is it like heat treating on SS??)
Please verify that HAVE is correct.
Thanks for your reply, Gary Silver